ABS-M30



ABS-M30

L’ABS-M30 è un materiale ideale per la modellazione concettuale, i prototipi funzionali, le attrezzature di produzione e per componenti pronti all’uso. L’ ABS-M30 ha una maggiore resistenza alla trazione, all’impatto e alla flessione dell’ABS standard. L’incollaggio tra gli strati è significativamente più resistente di quello dell’ABS per una durata maggiore dei componenti. Tutto ciò si traduce in test funzionali più realistici e pezzi di maggiore qualità. Disponibile in vari colori.

Mechanical Properties1 Test Method English Metric
Tensile Strength (Type 1, 0.125”, 0.2”/min) ASTM D638 5,200 psi 36 MPa
Tensile Modulus (Type 1, 0.125”, 0.2”/min) ASTM D638 350,000 psi 2,413 MPa
Tensile Elongation (Type 1, 0.125”, 0.2”/min) ASTM D638 4% 4%
Flexural Strength (Method 1, 0.05”/min) ASTM D790 8,800 psi 61 MPa
Flexural Modulus (Method 1, 0.05”/min) ASTM D790 336,000 psi 2,317 MPa
IZOD Impact, notched (Method A, 23°C) ASTM D256 2.6 ft-lb/in 139 J/m
IZOD Impact, un-notched (Method A, 23°C) ASTM D256 5.3 ft-lb/in 283 J/m
Thermal Properties3 Test Method English Metric
Heat Deflection (HDT) @ 66 psi, 0.125" unannealed ASTM D648 204°F 96°C
Heat Deflection (HDT) @ 264 psi, 0.125" unannealed ASTM D648 180°F 82°C
Vicat Softening Temp. (Rate B/50) ASTM D1525 210°F 99°C
Coefficient of Thermal Expansion (fl ow) ASTM E831 4.9E-05 in/in/°F 8.82E-05 mm/mm/°C
Coefficient of Thermal Expansion (xfl ow) ASTM E831 4.7E-05 in/in/°F 8.46E-05 mm/mm/°C
Glass Transition (Tg) DSC (SSYS) 226°F 108°C
Melt Point - - - - - - - - - Not Applicable2 Not Applicable2
Other3 Test Method Value Available Colors
Specific Gravity ASTM D792 1.04
Ivory
Gray
White
Red
Black
Blue
Flame Classification UL 94 HB (0.06", 1.5 mm)
Rockwell Hardness ASTM D785 109.5
Dielectric Strength IEC 60112 28.0 kV/mm

1 Build orientation is on side long edge
2 Due to amorphous nature, material does not display a melting point
3 Literature value unless otherwise noted
4 All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaque were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly result of the difference in properties of test plaques in the flat vs. vertical orientation.
The information presented are typical values intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes.
End-use material performance can be impacted (+/-) by, but not limited to, part design, end-use conditions, etc. Actual values will vary with build conditions.
Product specifications are subject to change without notice.
The performance characteristics of these materials may vary according to application, operating conditions, or end use. Each user is responsible for determining that the material is safe, lawful and technical suitable for the intended laws and regulations. Zare makes no warranties of any kind, express or implied, including, but not limited to, the warranties of merchantability, fitness for a particular use, or warranty against patent infringement.
All information contained in this document were supplied by Stratasys Inc. Copyright© 2013
All Trademarks included in this document are property of the respective owner